JIAZHI^® easy-cleaning functional resin

Model number
JIAZHI^®JZ-9540-20

Specification
Composition: Silicone modified hydroxyl acrylic resin solution
Appearance: Transparent to slight yellowish liquid
Solvent: BAC/PMA
Content: 50±3%(140℃ 2h)
Viscosity: 100-1000mPa·s(Rotating viscometer)(25±0.2)℃
Hydroxyl value: 170±5 mg KOH/g(Theoretical value of solid resin)
Note: This datasheet is intended to give typical results, not standard.Subject to COA.

Application system
Solvent-based system

Properties
●Increase slip. Improve hydrophobicity and oleophobicity.
●Provide anti-marker wiping performance.
●Provide lotus effect.
●Excellent flexibility.
●Excellent hot self-healing and room temperature healing.
●Water contact angle＞100°
●Excellent weather resistance.

Storage stability
Store in a cool, dry place in the unopened original packaging for 36 months. Products that exceed the storage period can continue to be used after passing the inspection. It must be closed immediately after use.

Recommended formula
1. Suggestion for PU varnish formulation

Remark:
1.1 NCO% of N3390=19.6, produced by Covestro, Germany.
1.2 After mixing A and B components, the storage period is 5-7 hours under the condition of a lid. Therefore, mixed materials should be used as soon as possible, otherwise it will be gelatinized and cannot be used.
1.3 Recommended baking temperature:
Paint protection film coatings: After baking at 100-130°C for 2-3 minutes, cool and rewind, and continue to mature at 60-80°C. The higher the temperature and the longer the time, the better the effect.
Note: The effect of stain resistance and chemical resistance depends on whether the coating is fully cross-linked; it is an effective way to put the surface-treated film in curing box for mature. At least 24 hours, if it can reach more than 48 hours, the effect will be better.
Other Industrial coatings: 80°C for 1 hour or 150°C for 5 minutes.

Package
25KG / 180KG