XOANONS® Polyether modified silicon leveling agent

Model number
XOANONS®WE-D577

Specification
Composition: Polyether modified polydimethyl siloxane
Appearance: slight yellowish clear liquid(paste at low temperature)
Solvent: ----
Density: 0.98-1.02g/ml(25±1)℃
Viscosity: 30-90s(Tu viscometer)(25±0.2)℃
Active content: 100%
Flash point: ＞100℃
Note: This data sheet is intended to give typical results, not standard.Subject to COA.

Application system
Solvent-based, UV Cure

Properties
?Provide a strong reduction of the surface tension.
?Reduce the friction coefficient. Increase slip and improve scratch resistance.
?Good re-coating and minimal influence on adhesion of coating films.
?Excellent resistance to shrinkage, often used as a replacement for oil resists without affecting the environment or recoatability.
?Hazy and viscous may occur at low temperatures. It would become clear and flow after heated. This will not influence the quality.

Incorporation
Diluted before addition, added in any stage including post-adding.

Suggest addition
Addition to total formulation 0.05-0.5%

Storage stability
Keep intact 24 months in original package.Products beyond the storage period may continue to be used after inspection. The container must be closed immediately after use.

Application recommendation
Transparency in varnish 1
Defoaming 2
Dynamic surface tension 5
Static surface tension 5
Slip 5
Prevent orange peel 1
0=unavailable 5=very effective

Package
25KG / 180KG